Alumon Gold 4N
Alumon Gold 4N is a ferrioxalate-based preparation in powder form. This product is for attaining gold shades of high fastness on artificially produced aluminium oxide film.
Commercial form | greenish yellow powder |
Storage stability | practically unlimited. Protect product from effects of light and moisture. Any lumps that may form have no influence on the product's dyeing properties. |
Solubility at 25°C
at 65°C |
430 g/l water
750 g/l water |
Bulk density | 550 g/l |
pH of product | 4.0 ± 0.5 at 30 g/l |
Applicable condition are as: | |
Anodic coating thickness | 10-25 microns |
Concentration |
5 – 15 g/l (Pale) 15 – 30 g/l (Medium to Deep) |
pH Range | 4.5 - 6.0 |
Buffering | Sodium Acetate or Acetic Acid |
Dye bath temperature | 40° - 55° C |
Immersion time | 2 – 20 minutes (depending upon Shade) |
SEALING:
The dyed oxide film must be properly sealed properly using a hot sealing salt ANO SEAL CA-350 for best result.
Other Recommendation:
- Ammonium compounds shall not be used for controlling of the pH or to buffer dye bath solution.
- The presence of ammonium compounds in the sealing solution may cause leaching and loss of color.
- Use sodium acetate for dye buffer.
- Adequate care to be taken for proper rinsing to control drag-in for optimum tank life.
- Dye may be dissolved separately outside the dye bath. Use demineralized water for better dye bath stability.
- The life of dye bath is reduced by water containing ammonium.